Description
Technical Parameters
Product Introduction
Tabular alumina is made of more than 98% industrial alumina powder (Al2O3) and a small amount of iron oxide, silicon oxide. It is a white abrasive that melts at high temperatures. Its hardness is slightly higher than that of brown corundum and its toughness is slightly lower. In the arc smelting cooling more than 2000 degrees, grinding molding, magnetic separation in addition to iron, sieve is made into a variety of particle size. It has dense texture, high hardness and sharp shape. Suitable for manufacturing ceramics, resin abrasives, grinding, polishing, sandblasting, precision casting (precision casting corundum), etc.
Advantages
Resistant to alkaline and inorganic acids
Excellent thermal shock resistance
Good wear resistance.
High volume stability
Water absorption is less than 1%
High hardness, high toughness
High thermal conductivity
High bending strength
Basic Information
|
Model No |
ZBHA |
||||||
|
Bulk density |
3.5kg/cm³ |
||||||
|
Moisure |
1.5% |
||||||
|
Specification |
5-8/10mm, 3-5/6mm ,1-3mm, 0-1mm ,325mesh |
||||||
|
Origin |
China |
||||||
|
Production capacity |
15000 tons |
||||||
|
Color |
White |
||||||
|
Porosity |
5% |
||||||
|
Transport Package |
Jumbo bag |
||||||
|
Trade Mark |
HUAO |
||||||
|
HS code |
281810900 |
|
Composition Type |
Al2O3% |
SiO2 % |
Na2O % |
Fe2O3 % |
Bulk density (g\cm3) |
Porosity % |
Moisture % |
|
MA-35 |
≥99.2 |
≤0.20 |
≤0.40 |
≤0.10 |
≥3.50 |
≤5.0 |
≤1.50 |
|
Typical value |
99.5 |
0.1 |
0.36 |
0.08 |
3.55 |
3.6 |
1 |